Production standards:
High coating adhesion, no spalling of coating, no micro chipping of cutting edge, Five inspections to ensure production standards.
Five inspections:
→1. Mixed material inspection. → 2. Blank inspection after pressing. →3. Blank inspection after sintering.
→4. Blank inspection before coating. →5. Full inspection of finished product after coating
Grade recommendation | Grade Introduction | Always stock available | Vc(m/min) | Fn(mm/r) | Ap(mm) |
| YP752 | 1. TiALSIN muti-coating 2. high coating hardness and high temperature resistance provide effective protection for cutting edges 3. Suitable for milling processing above HRC 40
| CNMG120404-FM | 160(80-200) | 0.15(0.05-0.3) | 1.0(0.1-2.0) |
| CNMG120408-FM | 160(80-200) | 0.15(0.05-0.3) | 2.5(0.5-4.0) | ||
| CNMG120412-FM | 160(80-200) | 0.15(0.05-0.3) | 3.0(0.5-4.0) | ||
| YP753 | 1. nc-TiAlN Coating,Special coating treatment 2. the coating has higher bonding force 3. improved the wear resistance and the heat insulation of the inserts 4. Suitable for medium and high speed machining 5. Suitable for stainless steel inserts and milling inserts. 6. Suitable for machining soft steel with a certain degree of adhesion | CNMG120404-FM | 160(80-200) | 0.15(0.05-0.3) | 1.0(0.1-2.0) |
| CNMG120408-FM | 160(80-200) | 0.15(0.05-0.3) | 2.5(0.5-4.0) | ||
| CNMG120412-FM | 160(80-200) | 0.15(0.05-0.3) | 3.0(0.5-4.0) | ||
Matching tool holder | |||||
|
|
| |||
| MCBNR/L | MCLNR/L | S type-MCLNR/L |